Size-dependence of silicon nanoparticle etching: Surprisingly rapid hydrogen generation and novel intermediate structures.

紀錄類型:	書目-電子資源 : Monograph/item
正題名/作者:	Size-dependence of silicon nanoparticle etching: Surprisingly rapid hydrogen generation and novel intermediate structures.
作者:	LaJoie, Krystal.
面頁冊數:	38 p.
附註:	Source: Masters Abstracts International, Volume: 52-01.
附註:	Advisers: Mark Swihart; Carl Lund.
Contained By:	Masters Abstracts International52-01(E).
標題:	Engineering, Chemical.
電子資源:	http://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=1539843
ISBN:	9781303160202

Size-dependence of silicon nanoparticle etching: Surprisingly rapid hydrogen generation and novel intermediate structures.
LaJoie, Krystal.

Size-dependence of silicon nanoparticle etching: Surprisingly rapid hydrogen generation and novel intermediate structures. - 38 p.

Source: Masters Abstracts International, Volume: 52-01.

Thesis (M.S.)--State University of New York at Buffalo, 2013.

Many phenomena involving silicon nanoparticles have demonstrated size-dependence. The efficiency and rate of water splitting to form hydrogen gas by oxidation of silicon are much greater for 10 nm silicon nanocrystals than for larger silicon particles. In the work presented here, silicon nanocrystals of &sim;10 nm in diameter produced hydrogen 150 times faster than 100 nm silicon, greatly exceeding the expected 10-fold increase expected from increased surface area. Hydrogen surface termination results in particles generating hydrogen gas in excess of the theoretical stoichiometric yield of 2 mol H2 per mol of Si. Transmission electron microscopy (TEM) and powder x-ray diffraction (XRD) show that 10 nm silicon particles are etched isotropically, in contrast to larger particles that etch anisotropically. A change in etching mechanism results in surprisingly rapid rates of etching and hydrogen generation. Silicon nanoparticles <100 nm in diameter and <40 microm in diameter were etched to quantify the size-dependence of hydrogen generation. TEM imaging was used to observe partially etched samples and gain insights into the etching process. Images of partially etched <100 nm silicon particles show hollow nanocapsule structures, markedly different from the solid nanospheres observed before reaction. These nanocapsules have oriented silicon walls. Formation of hollow structures was observed with different etchant types and concentrations, but the morphology of the nanocapsules depended on the etchant type and concentration. Hydrazine, KOH and NaOH form hollow nanospheres, nanoballoons and ruptured nanoballoons respectively when reacted with <100 nm particles. Hollow core formation is size-dependent and was not observed using 10 nm particles or microsilicon particles with any of the three etchants. Both hydrogen generation and nanocapsule formation exhibit qualitative size dependence, with instantaneous hydrogen generation only from 10 nm particles, and hollow capsule formation only with <100 nm particles.

ISBN: 9781303160202Subjects--Topical Terms:

226989
Engineering, Chemical.

Size-dependence of silicon nanoparticle etching: Surprisingly rapid hydrogen generation and novel intermediate structures.
LDR:02949nmm a2200277 4500 001 419204
005 20140520123956.5
008 140717s2013 ||||||||||||||||| ||eng d
020 $a 9781303160202
035 $a (MiAaPQ)AAI1539843
035 $a AAI1539843
040 $a MiAaPQ $c MiAaPQ
100 1 $a LaJoie, Krystal. $3 660183
245 1 0 $a Size-dependence of silicon nanoparticle etching: Surprisingly rapid hydrogen generation and novel intermediate structures.
300 $a 38 p.
500 $a Source: Masters Abstracts International, Volume: 52-01.
500 $a Advisers: Mark Swihart; Carl Lund.
502 $a Thesis (M.S.)--State University of New York at Buffalo, 2013.
520 $a Many phenomena involving silicon nanoparticles have demonstrated size-dependence. The efficiency and rate of water splitting to form hydrogen gas by oxidation of silicon are much greater for 10 nm silicon nanocrystals than for larger silicon particles. In the work presented here, silicon nanocrystals of &sim;10 nm in diameter produced hydrogen 150 times faster than 100 nm silicon, greatly exceeding the expected 10-fold increase expected from increased surface area. Hydrogen surface termination results in particles generating hydrogen gas in excess of the theoretical stoichiometric yield of 2 mol H2 per mol of Si. Transmission electron microscopy (TEM) and powder x-ray diffraction (XRD) show that 10 nm silicon particles are etched isotropically, in contrast to larger particles that etch anisotropically. A change in etching mechanism results in surprisingly rapid rates of etching and hydrogen generation. Silicon nanoparticles <100 nm in diameter and <40 microm in diameter were etched to quantify the size-dependence of hydrogen generation. TEM imaging was used to observe partially etched samples and gain insights into the etching process. Images of partially etched <100 nm silicon particles show hollow nanocapsule structures, markedly different from the solid nanospheres observed before reaction. These nanocapsules have oriented silicon walls. Formation of hollow structures was observed with different etchant types and concentrations, but the morphology of the nanocapsules depended on the etchant type and concentration. Hydrazine, KOH and NaOH form hollow nanospheres, nanoballoons and ruptured nanoballoons respectively when reacted with <100 nm particles. Hollow core formation is size-dependent and was not observed using 10 nm particles or microsilicon particles with any of the three etchants. Both hydrogen generation and nanocapsule formation exhibit qualitative size dependence, with instantaneous hydrogen generation only from 10 nm particles, and hollow capsule formation only with <100 nm particles.
590 $a School code: 0656.
650 4 $a Engineering, Chemical. $3 226989
650 4 $a Engineering, Materials Science. $3 226940
690 $a 0542
690 $a 0794
710 2 $a State University of New York at Buffalo. $b Chemical and Biological Engineering. $3 660184
773 0 $t Masters Abstracts International $g 52-01(E).
790 $a 0656
791 $a M.S.
792 $a 2013
793 $a English
856 4 0 $u http://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=1539843