Steel corrosion-induced concrete cra...
~
Jin, Weiliang,
Steel corrosion-induced concrete cracking
紀錄類型:
書目-電子資源 : Monograph/item
正題名/作者:
Steel corrosion-induced concrete crackingYuxi Zhao, Weiliang Jin.
作者:
Zhao, Yuxi,
其他作者:
Jin, Weiliang,
出版者:
Oxford, UK :Butterworth-Heinemann is an imprint of Elsevier,2016.
面頁冊數:
1 online resource (xxiv, 180 p.) :ill. (some col.)
附註:
5.2.1 Reinforced Concrete Specimens.
標題:
ConcreteTesting.
電子資源:
https://www.sciencedirect.com/science/book/9780128091975
ISBN:
9780128092101 (electronic bk.)
Steel corrosion-induced concrete cracking
Zhao, Yuxi,
Steel corrosion-induced concrete cracking
[electronic resource] /Yuxi Zhao, Weiliang Jin. - Oxford, UK :Butterworth-Heinemann is an imprint of Elsevier,2016. - 1 online resource (xxiv, 180 p.) :ill. (some col.)
5.2.1 Reinforced Concrete Specimens.
Includes bibliographical references and index.
Front Cover; Steel Corrosion-Induced Concrete Cracking; Copyright Page; Contents; Foreword; Preface; Acknowledgments; List of Figures; List of Tables; 1 Introduction; 1.1 Background; 1.2 Empirical Models; 1.2.1 Critical Steel Corrosion at Surface Cracking; 1.2.2 Crack Width at the Concrete Surface; 1.2.3 Discussion on the Empirical Models; 1.3 Analytical Models; 1.3.1 Three-Stage Corrosion-Induced Cracking Model; 1.3.2 Corrosion Products Filling Stage; 1.3.3 Concrete Cover Stressing and Cracking; 1.3.4 Rust Filling in Corrosion-Induced Cracks; 1.4 Contents of This Book; References.
Annotation'Steel Corrosion Induced Concrete Cracking' presents the latest advances in the origin, mechanism and development of corrosion-induced cracking in concrete. It investigates topics including expansion coefficient and elastic modulus of steel corrosion, rust layer and rust distribution, spatial distribution of corrosion products, and the shape of corrosion-induced cracks.
ISBN: 9780128092101 (electronic bk.)
LCCN: 2017303575Subjects--Topical Terms:
190342
Concrete
--Testing.Index Terms--Genre/Form:
533184
Electronic book.
LC Class. No.: TA440 / .S7947 2016eb
Dewey Class. No.: 620.1/366
Steel corrosion-induced concrete cracking
LDR
:04402cmm a2200325 a 4500
001
601422
006
m o d
007
cr cnu---unuuu
008
211110s2016 enka gob 001 0 eng d
010
$a
2017303575
020
$a
9780128092101 (electronic bk.)
020
$a
0128092106 (electronic bk.)
020
$a
9780128091975
020
$a
0128091975
035
$a
ocn945136155
040
$a
EBLCP
$b
eng
$c
EBLCP
$d
CDX
$d
IDEBK
$d
N
$d
YDXCP
$d
OPELS
$d
OCLCF
$d
KNOVL
$d
COO
$d
REB
$d
VLB
$d
OCLCO
$d
ZCU
$d
DEBSZ
$d
IDB
$d
OCLCQ
$d
U3W
$d
D6H
$d
CEF
$d
RRP
$d
OCLCQ
$d
WYU
$d
OCLCA
$d
AU@
$d
ABC
$d
UKMGB
$d
OCLCQ
$d
OCLCA
$d
MM9
$d
VT2
041
0
$a
eng
050
4
$a
TA440
$b
.S7947 2016eb
082
0 4
$a
620.1/366
$2
23
100
1
$a
Zhao, Yuxi,
$e
author.
$3
896463
245
1 0
$a
Steel corrosion-induced concrete cracking
$h
[electronic resource] /
$c
Yuxi Zhao, Weiliang Jin.
260
$a
Oxford, UK :
$b
Butterworth-Heinemann is an imprint of Elsevier,
$c
2016.
300
$a
1 online resource (xxiv, 180 p.) :
$b
ill. (some col.)
500
$a
5.2.1 Reinforced Concrete Specimens.
504
$a
Includes bibliographical references and index.
505
0
$a
Front Cover; Steel Corrosion-Induced Concrete Cracking; Copyright Page; Contents; Foreword; Preface; Acknowledgments; List of Figures; List of Tables; 1 Introduction; 1.1 Background; 1.2 Empirical Models; 1.2.1 Critical Steel Corrosion at Surface Cracking; 1.2.2 Crack Width at the Concrete Surface; 1.2.3 Discussion on the Empirical Models; 1.3 Analytical Models; 1.3.1 Three-Stage Corrosion-Induced Cracking Model; 1.3.2 Corrosion Products Filling Stage; 1.3.3 Concrete Cover Stressing and Cracking; 1.3.4 Rust Filling in Corrosion-Induced Cracks; 1.4 Contents of This Book; References.
505
8
$a
2 Steel Corrosion in Concrete2.1 Introduction; 2.2 Mechanisms of Steel Corrosion in Concrete; 2.2.1 Corrosion Process; 2.2.2 Corrosion Rate; 2.2.3 Passivation; 2.3 Steel Corrosion Induced by Carbonation or Chloride Attack; 2.3.1 Carbonation-Induced Corrosion; 2.3.2 Chloride-Induced Corrosion; 2.4 Corrosion Products; 2.5 Steel Corrosion-Induced Concrete Damage; 2.6 Conclusions; References; 3 The Expansion Coefficients and Modulus of Steel Corrosion Products; 3.1 Introduction; 3.2 Expansion Coefficient of Steel Corrosion Products; 3.2.1 Experimental Program; 3.2.2 Tested Results.
505
8
$a
3.2.2.1 X-Ray Diffraction3.2.2.2 Thermogravimetric Analysis; 3.2.2.3 Differential Thermal Analysis; 3.2.3 Composition of Rust Samples; 3.2.3.1 Influencing Factors; 3.2.3.2 Improving Rust Composition Analysis Using the TG Technique; 3.2.4 Expansion Coefficient of Rust Samples; 3.2.4.1 Classification of Hydroxy-oxides and Oxides; 3.2.4.2 Types of Hydroxy-oxides and Oxides; 3.2.4.3 Expansion Coefficients for Rust Samples; 3.2.4.4 Rust Expansion Coefficients in Different Environments; 3.3 Modulus of Steel Corrosion Products in Concrete; 3.3.1 Experimental Program.
505
8
$a
3.3.2 Loading and Unloading Stress-Strain Curve3.3.3 Tested Data of Cyclic Low-Compression Test; 3.3.4 Modulus of Rust; 3.4 Conclusions; References; 4 Damage Analysis and Cracking Model of Reinforced Concrete Structures with Rebar Corrosion; 4.1 Introduction; 4.2 Basic Concrete Cracking Model Due to Steel Corrosion; 4.3 Noncracking Stage of Corrosion-Induced Concrete Cracking Process; 4.4 Partial Cracking Stage of Corrosion-Induced Concrete Cracking Process; 4.4.1 Intact Part; 4.4.2 Cracked Part; 4.5 Corrosion-Induced Expansive Pressure.
505
8
$a
4.5.1 Relation Between Expansive Pressure and Steel Corrosion4.5.2 Variation of Expansive Pressure; 4.5.3 Effect of Concrete Cover Thickness; 4.5.4 Effect of Steel Bar Diameter; 4.5.5 Effect of Concrete Quality; 4.6 Discussion on the Radial Loss of Steel Bar; 4.6.1 Steel Loss Varying with the Crack Length; 4.6.2 Effect of Concrete Cover Thickness; 4.6.3 Effect of Steel Bar Diameter; 4.6.4 Effect of Rust Expansion Coefficient; 4.6.5 Effect of Concrete Quality; 4.7 Conclusions; References; 5 Mill Scale and Corrosion Layer at Concrete Surface Cracking; 5.1 Introduction; 5.2 Experimental Program.
520
8
$a
Annotation
$b
'Steel Corrosion Induced Concrete Cracking' presents the latest advances in the origin, mechanism and development of corrosion-induced cracking in concrete. It investigates topics including expansion coefficient and elastic modulus of steel corrosion, rust layer and rust distribution, spatial distribution of corrosion products, and the shape of corrosion-induced cracks.
650
0
$a
Concrete
$x
Testing.
$3
190342
650
0
$a
Reinforcing bars
$x
Corrosion.
$3
201859
650
0
$a
Concrete
$x
Corrosion.
$3
289985
650
0
$a
Concrete
$x
Deterioration.
$3
454321
650
0
$a
Concrete
$x
Cracking.
$3
195872
650
0
$a
Concrete
$x
Fracture.
$3
896465
650
7
$a
TECHNOLOGY & ENGINEERING
$x
Engineering (General)
$2
bisacsh
$3
896251
650
7
$a
TECHNOLOGY & ENGINEERING
$x
Reference.
$2
bisacsh
$3
896458
650
7
$a
Beton
$2
gnd
$3
896466
650
7
$a
Rissverhalten
$2
gnd
$3
896467
650
7
$a
Betonstahl
$2
gnd
$3
896468
650
7
$a
Korrosion
$2
gnd
$3
896469
655
0
$a
Electronic book.
$2
local
$3
533184
655
4
$a
Electronic books.
$2
local.
$3
214472
700
1
$a
Jin, Weiliang,
$e
author.
$3
896464
856
4 0
$u
https://www.sciencedirect.com/science/book/9780128091975
筆 0 讀者評論
全部
電子館藏
館藏
1 筆 • 頁數 1 •
1
條碼號
館藏地
館藏流通類別
資料類型
索書號
使用類型
借閱狀態
預約狀態
備註欄
附件
000000200678
電子館藏
1圖書
電子書
EB TA440 .S7947 2016eb 2016
一般使用(Normal)
編目處理中
0
1 筆 • 頁數 1 •
1
多媒體
多媒體檔案
https://www.sciencedirect.com/science/book/9780128091975
評論
新增評論
分享你的心得
Export
取書館別
處理中
...
變更密碼
登入