球化退火處理對扣件用40ACR合金鋼之球化率、顯微組織與機械性質之影響 ...
~
國立高雄大學化學工程及材料工程學系碩士班
球化退火處理對扣件用40ACR合金鋼之球化率、顯微組織與機械性質之影響 = Effect of spheroidizing annealing on sphericity, microstructure and mechanical properties of 40ACR steel for fastener manufacturing
紀錄類型:
書目-語言資料,印刷品 : 單行本
並列題名:
Effect of spheroidizing annealing on sphericity, microstructure and mechanical properties of 40ACR steel for fastener manufacturing
作者:
李旻哲,
其他團體作者:
國立高雄大學
出版地:
[高雄市]
出版者:
國立高雄大學;
出版年:
2015[民104]
面頁冊數:
[8],106葉圖,表 : 30公分;
標題:
40ACR
標題:
40ACR
電子資源:
https://hdl.handle.net/11296/4jamja
附註:
109年11月18日公開
球化退火處理對扣件用40ACR合金鋼之球化率、顯微組織與機械性質之影響 = Effect of spheroidizing annealing on sphericity, microstructure and mechanical properties of 40ACR steel for fastener manufacturing
李, 旻哲
球化退火處理對扣件用40ACR合金鋼之球化率、顯微組織與機械性質之影響
= Effect of spheroidizing annealing on sphericity, microstructure and mechanical properties of 40ACR steel for fastener manufacturing / 李旻哲撰 - [高雄市] : 國立高雄大學, 2015[民104]. - [8],106葉 ; 圖,表 ; 30公分.
109年11月18日公開.
參考書目:葉95-97.
40ACR40ACR
球化退火處理對扣件用40ACR合金鋼之球化率、顯微組織與機械性質之影響 = Effect of spheroidizing annealing on sphericity, microstructure and mechanical properties of 40ACR steel for fastener manufacturing
LDR
:05447nam0a2200265 450
001
458241
005
20220310133822.0
010
0
$b
精裝
010
0
$b
平裝
100
$a
20151007d2015 k y0chiy50 e
101
0
$a
chi
$d
chi
$d
eng
102
$a
tw
105
$a
ak am 000yy
200
1
$a
球化退火處理對扣件用40ACR合金鋼之球化率、顯微組織與機械性質之影響
$d
Effect of spheroidizing annealing on sphericity, microstructure and mechanical properties of 40ACR steel for fastener manufacturing
$z
eng
$f
李旻哲撰
210
$a
[高雄市]
$c
國立高雄大學
$d
2015[民104]
215
0
$a
[8],106葉
$c
圖,表
$d
30公分
300
$a
109年11月18日公開
314
$a
指導教授:林東毅博士
320
$a
參考書目:葉95-97
328
$a
碩士論文--國立高雄大學化學工程及材料工程學系碩士班本實驗以40ACR經過一次球化處理與一次伸線處理的線材做為實驗的材料,進行不同溫度、時間的二次球化處理後,進行顯微組織的觀察、碳化物型態的分析與球化率的計算,再以硬度試驗及拉伸試驗探討其機械性質,並藉以說明不同二次球化處理的顯微組織、碳化物型態與球化率之差異對於機械性質之影響。實驗結果發現,未經二次球化處理的材料,組織存在著不連續的層狀組織,700℃、720℃、740℃二次球化處理的組織皆為球化率高於99%的球狀組織,而760℃二次球化處理的組織則因沃斯田鐵化使得冷卻至室溫時有層狀組織出現,球化率則低於99%。而從機械性質中可發現,700℃、720℃、740℃二次球化處理後材料的強度隨著球化溫度的上升而略微下降,而760℃二次球化處理後材料的硬度值與抗拉強度卻高於其它二次球化溫度的材料,其原因為不連續層狀組織的出現與碳化物中的鉻元素固溶回基地相中,使得強度上升。二次球化溫度740℃、球化時間6小時之材料,硬度值與抗拉強度最低,伸長率最高,為鍛造加工所需要的線材二次球化之最佳參數。本實驗以40ACR經過一次球化處理與一次伸線處理的線材做為實驗的材料,進行不同溫度、時間的二次球化處理後,進行顯微組織的觀察、碳化物型態的分析與球化率的計算,再以硬度試驗及拉伸試驗探討其機械性質,並藉以說明不同二次球化處理的顯微組織、碳化物型態與球化率之差異對於機械性質之影響。 實驗結果發現,未經二次球化處理的材料,組織存在著不連續的層狀組織,700{212B68}、720{212B68}、740{212B68}二次球化處理的組織皆為球化率高於99%的球狀組織,而760{212B68}二次球化處理的組織則因沃斯田鐵化使得冷卻至室溫時有層狀組織出現,球化率則低於99%。而從機械性質中可發現,700{212B68}、720{212B68}、740{212B68}二次球化處理後材料的強度隨著球化溫度的上升而略微下降,而760{212B68}二次球化處理後材料的硬度值與抗拉強度卻高於其它二次球化溫度的材料,其原因為不連續層狀組織的出現與碳化物中的鉻元素固溶回基地相中,使得強度上升。二次球化溫度740{212B68}、球化時間6小時之材料,硬度值與抗拉強度最低,伸長率最高,為鍛造加工所需要的線材二次球化之最佳參數。 In this experiment, we used the wire of 40ACR chromium steel material that has been once spheroidizing treatment and drawing. After the twice spheroidizing treatment of different temperatures and holding time, we observed microstructure, patterns of carbide analysis and calculation of the rate of the sphericity. After that we did the hardness test and tensile test to investigate the mechanical properties. And we comprehend the effect of microstructure, the different carbide type, sphericity and mechanical properties by different twice spheroidizing treatment. In the research, it was found the lamellar structure without the twice spheroidizing treatment. After twice spheroidizing treatment at 700 ℃, 720 ℃ and 740 ℃, all of the sphericity are higher than 99 %. Since 760 ℃ is the temperature above anstenitizing, the microstructure of 760 ℃ cooling to room temperature has appeared lamellar structure and the sphericity is less than 99%. From the mechanical properties we can found that the tensile strength of twice spheroidizing treatment at 700 ℃, 720 ℃ and 740 ℃ is slightly decreased by raised holding temperature. But the hardness and the tensile strength after twice spheroidizing treatment at 760 ℃ are higher than other parameter. The reason is the appearance of the lamellar structure and the chromium in carbides took place solid solution, so that the tensile strength rised. The material with twice spheroidizing treatment of 740 ℃ holding temperature and 6 hours holding time is the best one for forging industry because the properties of the lowest hardness, lowest tensile strength and the highest elongation.
510
1
$a
Effect of spheroidizing annealing on sphericity, microstructure and mechanical properties of 40ACR steel for fastener manufacturing
$z
eng
610
# 0
$a
40ACR
$a
碳化物形態
$a
球化率
$a
機械性質
610
# 1
$a
40ACR
$a
type of carbide
$a
sphericity
$a
mechanical properties
681
$a
008M/0019
$b
541208 4065
$v
2007年版
700
1
$a
李
$b
旻哲
$4
撰
$3
709497
712
0 2
$a
國立高雄大學
$b
化學工程及材料工程學系碩士班
$3
353898
801
0
$a
tw
$b
NUK
$c
20201109
$g
CCR
856
7 #
$u
https://hdl.handle.net/11296/4jamja
$z
電子資源
$2
http
筆 0 讀者評論
全部
博碩士論文區(二樓)
館藏
2 筆 • 頁數 1 •
1
條碼號
館藏地
館藏流通類別
資料類型
索書號
使用類型
借閱狀態
預約狀態
備註欄
附件
310002931593
博碩士論文區(二樓)
不外借資料
學位論文
TH 008M/0019 541208 4065 2015
一般使用(Normal)
在架
0
310002931601
博碩士論文區(二樓)
不外借資料
學位論文
TH 008M/0019 541208 4065 2015 c.2
一般使用(Normal)
在架
0
2 筆 • 頁數 1 •
1
多媒體
多媒體檔案
https://hdl.handle.net/11296/4jamja
評論
新增評論
分享你的心得
Export
取書館別
處理中
...
變更密碼
登入