Effect of Temperature on the Delamination and Performance of Monocrystalline Silicon Solar Cells.

Record Type:	Electronic resources : Monograph/item
Title/Author:	Effect of Temperature on the Delamination and Performance of Monocrystalline Silicon Solar Cells.
Author:	Panchal, Tarang Kiran.
Published:	Ann Arbor : ProQuest Dissertations & Theses, 2023
Description:	72 p.
Notes:	Source: Masters Abstracts International, Volume: 85-01.
Notes:	Advisor: Kim, Hansung.
Contained By:	Masters Abstracts International85-01.
Subject:	Cadmium telluride.
Online resource:	http://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=30540038
ISBN:	9798379882129

Effect of Temperature on the Delamination and Performance of Monocrystalline Silicon Solar Cells.
Panchal, Tarang Kiran.

Effect of Temperature on the Delamination and Performance of Monocrystalline Silicon Solar Cells. - Ann Arbor : ProQuest Dissertations & Theses, 2023 - 72 p.

Source: Masters Abstracts International, Volume: 85-01.

Thesis (M.Sc.)--Purdue University, 2023.

This item must not be sold to any third party vendors.

The solar cells degrade over time in the field due to various environmental conditions including temperature and humidity. Accelerated lifetime testing was used to test solar cells in a short period of time to obtain reliability and predict the lifetime. Accelerated lifetime testing was done on two 10-WATT ACOPOWER rigid mono crystalline silicon solar panel, 2 3-WATT semi-flexible monocrystalline silicon solar panel and 30 Sunyima Mini Monocrystalline Solar Cell to calculate the acceleration factor, mean reliable life through statistical analysis at certain working conditions. Two Damp heat tests were conducted on the samples to find the degradation and potential defects that occur in the solar cell and that data was used for the statistical analysis. Reliasoft ALTA software was used to statistically analyze the experimental data and to predict the lifetime and to find the probability of failure of the solar cells.Peeling tests were conducted to find the adhesion strength between layers of the untested solar cell samples and accelerated life testing (ALT) tested solar cell samples. Tensile tests were conducted to find out the Young’s Modulus, yield stress and yield strain of the peel arm from the peeling test. The data from the tests were used to calculate the energy release rate or the fracture energy. A multivariable Regression analysis was done to develop an analytical equation between the energy release rate (Gc) and Temperature & Humidity.

ISBN: 9798379882129Subjects--Topical Terms:

966910
Cadmium telluride.

Effect of Temperature on the Delamination and Performance of Monocrystalline Silicon Solar Cells.
LDR:02657nmm a2200409 4500 001 655804
005 20240414211935.5
006 m o d
007 cr#unu||||||||
008 240620s2023 ||||||||||||||||| ||eng d
020 $a 9798379882129
035 $a (MiAaPQ)AAI30540038
035 $a (MiAaPQ)Purdue22783613
035 $a AAI30540038
040 $a MiAaPQ $c MiAaPQ
100 1 $a Panchal, Tarang Kiran. $3 966909
245 1 0 $a Effect of Temperature on the Delamination and Performance of Monocrystalline Silicon Solar Cells.
260 1 $a Ann Arbor : $b ProQuest Dissertations & Theses, $c 2023
300 $a 72 p.
500 $a Source: Masters Abstracts International, Volume: 85-01.
500 $a Advisor: Kim, Hansung.
502 $a Thesis (M.Sc.)--Purdue University, 2023.
506 $a This item must not be sold to any third party vendors.
520 $a The solar cells degrade over time in the field due to various environmental conditions including temperature and humidity. Accelerated lifetime testing was used to test solar cells in a short period of time to obtain reliability and predict the lifetime. Accelerated lifetime testing was done on two 10-WATT ACOPOWER rigid mono crystalline silicon solar panel, 2 3-WATT semi-flexible monocrystalline silicon solar panel and 30 Sunyima Mini Monocrystalline Solar Cell to calculate the acceleration factor, mean reliable life through statistical analysis at certain working conditions. Two Damp heat tests were conducted on the samples to find the degradation and potential defects that occur in the solar cell and that data was used for the statistical analysis. Reliasoft ALTA software was used to statistically analyze the experimental data and to predict the lifetime and to find the probability of failure of the solar cells.Peeling tests were conducted to find the adhesion strength between layers of the untested solar cell samples and accelerated life testing (ALT) tested solar cell samples. Tensile tests were conducted to find out the Young’s Modulus, yield stress and yield strain of the peel arm from the peeling test. The data from the tests were used to calculate the energy release rate or the fracture energy. A multivariable Regression analysis was done to develop an analytical equation between the energy release rate (Gc) and Temperature & Humidity.
590 $a School code: 0183.
650 4 $a Cadmium telluride. $3 966910
650 4 $a Thermal cycling. $3 966902
650 4 $a Humidity. $3 966895
650 4 $a Failure. $3 915861
650 4 $a Solar energy. $3 242824
650 4 $a Electricity. $3 204307
650 4 $a Weather. $3 225024
650 4 $a Yield stress. $3 966911
650 4 $a Electric rates. $3 966912
650 4 $a Adhesion. $3 346049
650 4 $a Photovoltaic cells. $3 215308
650 4 $a Silicon wafers. $3 966897
650 4 $a Heat. $3 230291
650 4 $a Adhesives. $3 219293
650 4 $a Ultraviolet radiation. $3 355033
650 4 $a Corrosion. $3 921394
650 4 $a Alternative energy. $3 857402
650 4 $a Atmospheric sciences. $3 886604
650 4 $a Condensed matter physics. $3 708726
650 4 $a Energy. $3 212397
650 4 $a Industrial engineering. $3 200218
650 4 $a Meteorology. $3 276569
650 4 $a Physics. $3 179414
690 $a 0363
690 $a 0725
690 $a 0611
690 $a 0791
690 $a 0546
690 $a 0629
690 $a 0557
690 $a 0605
710 2 $a Purdue University. $3 966863
773 0 $t Masters Abstracts International $g 85-01.
790 $a 0183
791 $a M.Sc.
792 $a 2023
793 $a English
856 4 0 $u http://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=30540038